氮化铝/氧化石墨烯对环氧树脂胶黏剂导热性能的影响

Effects of Aluminium Nitride/Graphene Oxide on Thermal Conductivity of Epoxy Adhesive

摘要:

以环氧树脂为基体，氮化铝为导热填料制备了氮化铝/环氧树脂导热胶黏剂。采用傅里叶变换红外光谱仪、扫描电镜、热重分析仪、热常数分析仪对导热胶黏剂进行了表征。结果表明，改性后硅烷偶联剂分子成功枝接在氮化铝表面。改性后，氮化铝与环氧树脂的界面粘结力增强，热稳定性和导热性均得到明显改善。当氮化铝质量为导热胶黏剂质量的70%时，改性氮化铝/环氧树脂热胶黏剂的导热系数为2.24 W/(m.K)，而未改性氮化铝/环氧树脂的导热系数仅为1.73 W/(m.K)。为进一步提到其导热性能，制备了改性氮化铝/氧化石墨烯/环氧树脂导热胶黏剂，当改性氮化铝和氧化石墨烯的质量分数分别为50%和3%时，导热胶黏剂导热系数为3.05 W/(m.K)。

Abstract:

Aluminium nitride (AlN)/epoxy thermal conductive adhesive was prepared with epoxy as matrix material, AlN as thermal conductive filler. The structure and properties of adhesive were characterized using fourier transform infrared spectrometer, scanning electron microscopy, thermal gravimetric analyzer and thermal constants analyzer. The experimental results showed that coupling agent molecule was successfully chemically grafted onto the AlN surface. Modified AlN had strong interface adhesion with epoxy. The thermal stability and thermal conductivity of epoxy adhesive can be significantly improved by modified AlN. When the AlN mass fraction was 70%, the thermal conductivities of modified AlN/epoxy and AlN/epoxy adhesive were 2.24 W/(m.K) and 1.73 W/(m.K), respectively. In order to further improve thermal conductivity, hybrid filler of modified AlN and graphene oxide (GO) was employed to prepare thermal conductive adhesive. When the mass fractions of modified AlN and GO were 50% and 3%, the thermal conductivity of epoxy adhesive reached 3.05 W/(m.K).